Abstract

This research presents a novel methodology to classify copper tailings according to their potential as alkali-activated materials (AAMs) for construction applications. The methodology includes geochemical and mineralogical characterization via QEMSCAN and X-ray fluorescence, with mechanical performance evaluation through compressive strength test (UCS). A three-phase diagram based on Al2O3, Fe2O3, and CaO-MgO-K2O is proposed for a fast screening of copper tailing potential to be used as a construction material. In this paper, three copper tailings were chosen to test the methodology, and a set of five samples for each tailing have been geopolymerized for testing. Copper tailing samples were mixed with 0, 2.5, 5, 7.5 and 10% by mass of Ordinary Portland Cement (OPC) to evaluate the effect on performance when a chemical co-activator is used to improve material reactivity. Compressive strength testing was applied on 2 cm3 cubes after 28 days of curing at 60 °C, yielding values from 6 to 26.1 MPa. The best performing sample featured a Si/Al ≅ 3 ratio and a mineralogy with significant presence of reactive species such as plagioclase and K-feldspar (≅42%). In contrast, high levels of Fe2O3 (≥12%), clay (≥7%), and pyrite (≥4%) were associated with reduced mechanical performance. © 2025 by the authors.